This Article Alert me when this article is cited Alert me if a correction is posted Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Download to citation manager Citing Articles Citing Articles via Google Scholar Google Scholar Articles by Gyomorey, S. Articles by Winemaker, M. Search for Related Content PubMed Articles by Gyomorey, S. Articles by Winemaker, M.

POTENTIAL MECHANISM OF ORTHOPAEDIC IMPLANT WEAR PARTICLE INDUCED APOPTOSIS OF OSTEOBLASTS IN-VITRO

Hamilton Arthroplasty Group, Hamilton Health Sciences Henderson Hospital, 711 Concession St., Hamilton, ON L8V 1C3

To evaluate the mechanism by which orthopedic implant wear particles induce apoptosis in immature osteoblasts in an in-vitro setting.

Stromal cells from femurs of thirty day-old Swiss Webster Mice were isolated, cultured in-vitro, and incubated with orthopedic wear particles in the micrometer size range. After incubation with wear-particles, the cells were assessed for Caspase three expression and activity in the presence or absence of specific inhibitor(s) in order to delineate potential mechanism for cellular changes previously reported.

Here we report the induction of caspase three protein expression and activity with incubation of stromal cells with titanium wear particles. Caspase three activity however was not demonstrated to be up regulated in a time dependent manner or at lower concentration of particles (2 x 107 particles/ml). However, there was a significant (P<0.05) increase in caspase three activity with titanium particle at higher concentration (4 x 107 particles/ml) that was not reversible when the extrinsic arm of the apoptotic pathway was blocked with anti-TNFa antibodies.

Our previous studies have suggested that aseptic loosening of orthopedic implants may be independent of inflammatory processes, and may be associated with induction of programmed cell death. Our current results would strengthen this idea by demonstrating induction of expression and activity of caspase three involved in apoptosis in cells incubated with wear particles. In addition, titanium wear particles may induce apoptosis through direct cellular effects rather than through the extrinsic TNFa pathway. Delineating the mechanism by which wear particles induce apoptosis in immature osteoblasts will allow for the selection and/or development of inhibitors to the process of asceptic loosening by targeting a specific pathway.